Good Initial Strength Hot Melt Adhesive TPU Material Low Temperature Chemical Sheet Fabrics Lamination

Ask Latest Price
Video Channel
Brand Name :Dingzhi
Model Number :DHMA-98A-1
Certification :Reach,ISO
Place of Origin :China
MOQ :25kg
Price :please contact for details
Payment Terms :T/T, Western Union
Supply Ability :700Tons/ Month
Delivery Time :5-8 days
Packaging Details :waterproof bag, 25kg per bag; pallet, 1 tons per pallet
Material :Polyester based
Application :Low temperature chemical sheet, fire hose co-extrusion, ho tmelt adhesive film, fabrics lamination etc,
more
Contact Now

Add to Cart

Find Similar Videos
View Product Description

Hot melt adhesive material with good initial strength Low temperature chemical sheet fabrics lamination

Production Process:

Mold: Solvent processing, Injection molding, Extrusion molding, Calender

Drying requirements: Please dry at 90-100℃ for 3-4 hours;

Injection temperature: 190-195 degrees for the first section, 195-200 degrees for the second section, and 195-210 degrees for the third section

Features:

Excellent physical properties,

Good initial strength & solvent solubility,

Fast crystallization,

Low temperature lamination

Technical Datasheet:

Content Hardness 100%Modulus 300%Modulus Ring and Ball Softening Point Tear strength Tensile Strength Breaking Elongation
Test Method ISO R 868 ASTM D-412 ASTM D-412 ASTM D3461 ASTM D-624 ASTM D-412 ASTM D-412
Test units ShoreA/D mpa mpa N/mm Mpa %
DHMA-98A-1 98A 8 10 81 131 21 760
DHMA-98A-2 98A 8 13 75 135 22 735
DHMA-98A-3 98A 8 11 88 148 27 750
DHMA-98A-4 98A 8 11 79 150 25 760
DHMA-98A-5 98A 8 12 87 153 27 760

Application:

Low temperature chemical sheet, fire hose co-extrusion, ho tmelt adhesive film, fabrics lamination etc,

Dingzhi Polymer provide wide range of raw material, can be widely used in shoe materials, bag materials, sports equipment, medical equipment, the automobile industry, packaging products, wire and cable coating materials, hoses, films, coatings, inks, adhesives, melt spun spandex fibers, artificial leather, bonded clothing, gloves, air blowing products, agricultural greenhouse, air transportation, and national defense industry.

Please contact us for details.